	Conformances		Typical Results Of Mechanical Properties As Welded Metal				Typical Results Of Weld Metal Composition(wt %)										Remarks
LSE Series	GB/T 5117	AWS A5.5	Yield Strength (Mpa)	Tensile Strength (Mpa)	Elongation %	Charpy V-Notch J(℃)	C	Mn	Si	P	S	Cr	Ni	Mo
LSE-7018-W1	5018-NCC2	E7018-W1	468	558	26	137(-20℃)	0.082	0.620	0.550	0.011	0.009	0.280	0.330		V(0.05)	Cu(0.47)
LSE-8018-W2	5518-NCC1	E8018-W2	515	583	25	140(-20℃)	0.067	1.100	0.480	0.010	0.008	0.610	0.530			Cu(0.58)
LSE-8016-C1	E5516-N5 P	E8016-C1	473	568	26	88(-60℃)	0.072	0.910	0.370	0.011	0.009		2.510				605℃ Xlh
LSE-8018-C1	E5518-N5 P	E8018-C1	478	591	25	87(-60℃)	0.083	0.690	0.520	0.012	0.009		2.520				605℃ X1h
LSE-8016-C2	E5516-N7 P	E8016-C2	488	593	26	47(-75℃)	0.055	0.720	0.390	0.011	0.008		3.560				605℃ Xlh
LSE-8018-C2	E5518cN7 P	E8018-C2	506	598	25	66(-75℃)	0.064	0.810	0.590	0.009	0.007		3.600				605℃ X1h
LSE-8016-C3	E5516-N2	E8016-C3	487	590	25	118(-40℃)	0.073	1.020	0.580	0.012	0.008		0.890	0.009	V(0.007)
LSE-8018-C3	E5518-N2	E8018-C3	493	589	26	128(-40℃)	0.079	1.030	0.610	0.012	0.009		0.940	0.010	V(0.008)
LSE-8016-C4	E5516-N3 P	E8016-C4	502	597	24	98(-50℃)	0.080	1.060	0.510	0.009	0.008		1.670	0.010			620℃ X1h
LSE-8018-C4	E5518-N3 P	E8018-C4	501	598	23	101(-50℃)	0.078	1.080	0.620	0.010	0.009		1.550				620℃ X1h
	Conformances		Typical Results Of Mechanical Properties As Welded Metal				Typical Results Of Weld Metal Composition(wt %)										Remarks
LSE Series	GB/T 5118	AWS A5.5	Yield Strength (Mpa)	Tensile Strength (Mpa)	Elongation %	Charpy V-Notch J(℃)	C	Mn	Si	P	S	Cr	Ni	Mo	V		PWHT
LSE-7015-A1	E5015-1M3	E7015-A1	481	577	27	137(20℃)	0.086	0.770	0.460	0.011	0.008			0.560			620℃ X1h
LSE-7016-A1	E5016-1M3	E7016-A1	462	559	25	116(20℃)	0.063	0.680	0.510	0.012	0.009			0.540			620℃ X1h
LSE-7018-A1	5018-1M3	E7018-A1	479	584	26	146(20℃)	0.074	0.660	0.480	0.010	0.009			0.530			620℃ X1h
LSE-8015-B1	E5515-CM	E8015-B1	494	597	23	89(20℃)	0.083	0.760	0.590	0.011	0.008	0.610		0.560			690℃ X1h
LSE-8015-B2	5515-1CM	E8015-B2	492	595	22	137(20℃)	0.091	0.740	0.530	0.010	0.009	1.430		0.570			690℃ X1h
LSE-8015-B6	E5515-5CM	E8015-B6	491	597	21	118(20℃)	0.080	0.790	0.410	0.009	0.008	5.300	0.010	0.550			740℃ X1h
LSE-8015-B8	6215-9C1M	E8015-B8	556	697	22	93(20℃)	0.088	0.820	0.420	0.008	0.007	9.100	0.100	1.130			740℃ X1h
LSE-8016-B2	E5516-1CM	E8016-B2	483	579	21	133(20℃)	0.092	0.800	0.520	0.009	0.007	1.460		0.580			690℃ X1h
LSE-8018-B2	E5518-1CM	E8018-B2	458	586	22	129(20℃)	0.067	0.770	0.490	0.012	0.010	1.380		0.540			690℃ X1h
LSE-9015-B3	E6215-2C1M	E9015-B3	549	636	22	121(20℃)	0.075	0.830	0.570	0.009	0.008	2.210		1.120			690℃ X1h
LSE-9015-B91	E6215-9C1MV	E9015-B91	583	728	21	80(20℃)	0.094	1.210	0.260	0.009	0.007	9.200	0.510	1.100	0.220	Nb(0.07)	760℃ X2h
LSE-9015-B92	E6215-G	E9015-B92	567	725	20	71(20℃)	0.091	1.080	0.330	0.008	0.006	9.180	0.600	0.620	0.250	W(1.71)	760℃ X2h
LSE-9016-B3	E6216-2C1M	E9016-B3	558	641	22	36(20℃)	0.085	0.790	0.430	0.011	0.009	2.380		1.120			690℃ X1h
LSE-9018-B3	E6218-2C1M	E9018-B3	579	683	21	46(20℃)	0.085	0.690	0.730	0.012	0.009	2.370		1.11			690℃ X1h

Category：

Commodity

Contact

SMAW-Low Alloy

	Conformances		Typical Results Of Mechanical Properties As Welded Metal				Typical Results Of Weld Metal Composition(wt %)										Remarks
LSE Series	GB/T 5117	AWS A5.5	Yield Strength (Mpa)	Tensile Strength (Mpa)	Elongation %	Charpy V-Notch J(℃)	C	Mn	Si	P	S	Cr	Ni	Mo
LSE-7018-W1	5018-NCC2	E7018-W1	468	558	26	137(-20℃)	0.082	0.620	0.550	0.011	0.009	0.280	0.330		V(0.05)	Cu(0.47)
LSE-8018-W2	5518-NCC1	E8018-W2	515	583	25	140(-20℃)	0.067	1.100	0.480	0.010	0.008	0.610	0.530			Cu(0.58)
LSE-8016-C1	E5516-N5 P	E8016-C1	473	568	26	88(-60℃)	0.072	0.910	0.370	0.011	0.009		2.510				605℃ Xlh
LSE-8018-C1	E5518-N5 P	E8018-C1	478	591	25	87(-60℃)	0.083	0.690	0.520	0.012	0.009		2.520				605℃ X1h
LSE-8016-C2	E5516-N7 P	E8016-C2	488	593	26	47(-75℃)	0.055	0.720	0.390	0.011	0.008		3.560				605℃ Xlh
LSE-8018-C2	E5518cN7 P	E8018-C2	506	598	25	66(-75℃)	0.064	0.810	0.590	0.009	0.007		3.600				605℃ X1h
LSE-8016-C3	E5516-N2	E8016-C3	487	590	25	118(-40℃)	0.073	1.020	0.580	0.012	0.008		0.890	0.009	V(0.007)
LSE-8018-C3	E5518-N2	E8018-C3	493	589	26	128(-40℃)	0.079	1.030	0.610	0.012	0.009		0.940	0.010	V(0.008)
LSE-8016-C4	E5516-N3 P	E8016-C4	502	597	24	98(-50℃)	0.080	1.060	0.510	0.009	0.008		1.670	0.010			620℃ X1h
LSE-8018-C4	E5518-N3 P	E8018-C4	501	598	23	101(-50℃)	0.078	1.080	0.620	0.010	0.009		1.550				620℃ X1h
	Conformances		Typical Results Of Mechanical Properties As Welded Metal				Typical Results Of Weld Metal Composition(wt %)										Remarks
LSE Series	GB/T 5118	AWS A5.5	Yield Strength (Mpa)	Tensile Strength (Mpa)	Elongation %	Charpy V-Notch J(℃)	C	Mn	Si	P	S	Cr	Ni	Mo	V		PWHT
LSE-7015-A1	E5015-1M3	E7015-A1	481	577	27	137(20℃)	0.086	0.770	0.460	0.011	0.008			0.560			620℃ X1h
LSE-7016-A1	E5016-1M3	E7016-A1	462	559	25	116(20℃)	0.063	0.680	0.510	0.012	0.009			0.540			620℃ X1h
LSE-7018-A1	5018-1M3	E7018-A1	479	584	26	146(20℃)	0.074	0.660	0.480	0.010	0.009			0.530			620℃ X1h
LSE-8015-B1	E5515-CM	E8015-B1	494	597	23	89(20℃)	0.083	0.760	0.590	0.011	0.008	0.610		0.560			690℃ X1h
LSE-8015-B2	5515-1CM	E8015-B2	492	595	22	137(20℃)	0.091	0.740	0.530	0.010	0.009	1.430		0.570			690℃ X1h
LSE-8015-B6	E5515-5CM	E8015-B6	491	597	21	118(20℃)	0.080	0.790	0.410	0.009	0.008	5.300	0.010	0.550			740℃ X1h
LSE-8015-B8	6215-9C1M	E8015-B8	556	697	22	93(20℃)	0.088	0.820	0.420	0.008	0.007	9.100	0.100	1.130			740℃ X1h
LSE-8016-B2	E5516-1CM	E8016-B2	483	579	21	133(20℃)	0.092	0.800	0.520	0.009	0.007	1.460		0.580			690℃ X1h
LSE-8018-B2	E5518-1CM	E8018-B2	458	586	22	129(20℃)	0.067	0.770	0.490	0.012	0.010	1.380		0.540			690℃ X1h
LSE-9015-B3	E6215-2C1M	E9015-B3	549	636	22	121(20℃)	0.075	0.830	0.570	0.009	0.008	2.210		1.120			690℃ X1h
LSE-9015-B91	E6215-9C1MV	E9015-B91	583	728	21	80(20℃)	0.094	1.210	0.260	0.009	0.007	9.200	0.510	1.100	0.220	Nb(0.07)	760℃ X2h
LSE-9015-B92	E6215-G	E9015-B92	567	725	20	71(20℃)	0.091	1.080	0.330	0.008	0.006	9.180	0.600	0.620	0.250	W(1.71)	760℃ X2h
LSE-9016-B3	E6216-2C1M	E9016-B3	558	641	22	36(20℃)	0.085	0.790	0.430	0.011	0.009	2.380		1.120			690℃ X1h
LSE-9018-B3	E6218-2C1M	E9018-B3	579	683	21	46(20℃)	0.085	0.690	0.730	0.012	0.009	2.370		1.11			690℃ X1h

Add:Starland Building, No.168 Yunhui Road, SIP, Suzhou
Tel:+86 512-66030258
Fax:+86 512-66059578
E-mail:june.guo@howey-tech.com

Product Message

无码人妻精品一区二区蜜桃网站丨嫖妓大龄熟妇正在播放丨日本熟妇乱人伦xxxx丨精品综合久久久久久8888丨久久久国产精品一区二区18禁

這里是標題一h1占位文字