| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 36034 | AWS A5.23 |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy V-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | |||||||||||||||||
| LW-Ni1K*LFX-201R | S49A/P5FB-SUN2 | F7A/P5-ENi1 | 427 | 521 | 33 | 41(-50℃) | 0.056 | 1.230 | 0.420 | 0.009 | 0.008 | 1.050 | |||||||||||||||||||
| LW-Ni3*LFX-201R | S49A/P7FB-SUN7 | F7A/P7-ENi3 | 439 | 548 | 31 | 77(-70℃) | 0.047 | 1.100 | 0.650 | 0.011 | 0.009 | 3.500 | |||||||||||||||||||
| LW-Ni5*LFX-201R | S55A/P5FB-SUN2 | F8A/P5-ENi5 | 521 | 593 | 32 | 88(-50℃) | 0.080 | 1.300 | 0.890 | 0.009 | 0.008 | 0.890 | 0.250 | ||||||||||||||||||
| LW-EF1*LFX-201R |
S62A/P4FB-SUN2M2 |
F9A/P4-EF1 | 557 | 629 | 25 | 91(-40℃) | 0.087 | 1.460 | 0.330 | 0.010 | 0.008 | 1.130 | 0.480 | ||||||||||||||||||
| LW-EF2*LFX-201R | S62A2FB-SUN1M3 | F9A2-EF2 | 590 | 649 | 23 | 83(-20℃) | 0.950 | 2.170 | 0.590 | 0.008 | 0.007 | 0.750 | 0.620 | ||||||||||||||||||
| LW-EF3*LFX-201R |
S62A/P4FB-SUN2M3 |
F9A/P4-EF3 | 588 | 660 | 25 | 101(-40℃) | 0.089 | 1.620 | 0.440 | 0.011 | 0.009 | 1.060 | 0.560 | ||||||||||||||||||
| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 12470 | AWSA523 |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy V-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | PWHT | ||||||||||||||||
| LW-EB2*LFX-201 | S55A/P2FB-SU1CM | F8P2-EB2 | 565 | 621 | 25 | 92(-20℃) | 0.090 | 0.880 | 1.170 | 0.011 | 0.008 | 1.150 | 0.550 | 690℃ X1h | |||||||||||||||||
| LW-EB3*LFX-201 | S62P2FB-SU2C1M | F9P2-EB3 | 546 | 633 | 23 | 98(-20℃) | 0.093 | 0.760 | 0.770 | 0.012 | 0.009 | 2.530 | 1.080 | 690℃ X1h | |||||||||||||||||
| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 5293 | AWS A5.23 |
Yield Strengtl (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy Y-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | |||||||||||||||||
| LW-EA2*LFX-201 | S55A/P2FB-SU2M3 | F8A/P2-EA2 | 534 | 621 | 26 | 108(-20℃) | 0.880 | 0.970 | 1.080 | 0.009 | 0.008 | 0.570 | |||||||||||||||||||
| LW-EA3*LFX-201 | S62A/P2FB-SU4M32 | F9A/P2-EA3 | 549 | 635 | 26 | 105(-20℃) | 0.960 | 1.550 | 0.720 | 0.013 | 0.007 | 0.565 | |||||||||||||||||||
| LW-EA4*LFX-201 | S55A/P3FB-SU3M3 | F8A/P2-EA4 | 518 | 602 | 25 | 98(-30℃) | 0.990 | 1.510 | 0.940 | 0.011 | 0.009 | 0.610 | |||||||||||||||||||
Category：
Commodity
SAW-Low Alloy
| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 36034 | AWS A5.23 |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy V-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | |||||||||||||||||
| LW-Ni1K*LFX-201R | S49A/P5FB-SUN2 | F7A/P5-ENi1 | 427 | 521 | 33 | 41(-50℃) | 0.056 | 1.230 | 0.420 | 0.009 | 0.008 | 1.050 | |||||||||||||||||||
| LW-Ni3*LFX-201R | S49A/P7FB-SUN7 | F7A/P7-ENi3 | 439 | 548 | 31 | 77(-70℃) | 0.047 | 1.100 | 0.650 | 0.011 | 0.009 | 3.500 | |||||||||||||||||||
| LW-Ni5*LFX-201R | S55A/P5FB-SUN2 | F8A/P5-ENi5 | 521 | 593 | 32 | 88(-50℃) | 0.080 | 1.300 | 0.890 | 0.009 | 0.008 | 0.890 | 0.250 | ||||||||||||||||||
| LW-EF1*LFX-201R |
S62A/P4FB-SUN2M2 |
F9A/P4-EF1 | 557 | 629 | 25 | 91(-40℃) | 0.087 | 1.460 | 0.330 | 0.010 | 0.008 | 1.130 | 0.480 | ||||||||||||||||||
| LW-EF2*LFX-201R | S62A2FB-SUN1M3 | F9A2-EF2 | 590 | 649 | 23 | 83(-20℃) | 0.950 | 2.170 | 0.590 | 0.008 | 0.007 | 0.750 | 0.620 | ||||||||||||||||||
| LW-EF3*LFX-201R |
S62A/P4FB-SUN2M3 |
F9A/P4-EF3 | 588 | 660 | 25 | 101(-40℃) | 0.089 | 1.620 | 0.440 | 0.011 | 0.009 | 1.060 | 0.560 | ||||||||||||||||||
| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 12470 | AWSA523 |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy V-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | PWHT | ||||||||||||||||
| LW-EB2*LFX-201 | S55A/P2FB-SU1CM | F8P2-EB2 | 565 | 621 | 25 | 92(-20℃) | 0.090 | 0.880 | 1.170 | 0.011 | 0.008 | 1.150 | 0.550 | 690℃ X1h | |||||||||||||||||
| LW-EB3*LFX-201 | S62P2FB-SU2C1M | F9P2-EB3 | 546 | 633 | 23 | 98(-20℃) | 0.093 | 0.760 | 0.770 | 0.012 | 0.009 | 2.530 | 1.080 | 690℃ X1h | |||||||||||||||||
| Conformances |
Typical Results Of Mechanical Properties As Welded Metal |
Typical Results Of Wire Composition(wt %) | Remarks | ||||||||||||||||||||||||||||
| LW/LFX Series | GB/T 5293 | AWS A5.23 |
Yield Strengtl (Mpa) |
Tensile Strength (Mpa) |
Elongation % |
Charpy Y-Notch J(℃) |
C | Mn | Si | P | S | Cr | Ni | Mo | |||||||||||||||||
| LW-EA2*LFX-201 | S55A/P2FB-SU2M3 | F8A/P2-EA2 | 534 | 621 | 26 | 108(-20℃) | 0.880 | 0.970 | 1.080 | 0.009 | 0.008 | 0.570 | |||||||||||||||||||
| LW-EA3*LFX-201 | S62A/P2FB-SU4M32 | F9A/P2-EA3 | 549 | 635 | 26 | 105(-20℃) | 0.960 | 1.550 | 0.720 | 0.013 | 0.007 | 0.565 | |||||||||||||||||||
| LW-EA4*LFX-201 | S55A/P3FB-SU3M3 | F8A/P2-EA4 | 518 | 602 | 25 | 98(-30℃) | 0.990 | 1.510 | 0.940 | 0.011 | 0.009 | 0.610 | |||||||||||||||||||